Description
ST-White super-translucent zirconia, for full-contour crowns & bridges
16 Shade and 7 Enhancement Liquids are Available for AxZir ST and TT Zirconia
| INDICATION | HT-WHITE | ST-WHITE | TT-WHITE |
| COPINGS | X | X | X |
| 2-4 UNIT FRAMEWORKS | X | X | 2-3 UNITS |
| 5-6 UNIT FRAMEWORKS** | X | X | – |
| CANTILEVER BRIDGE* | X | X | – |
| INLAY BRIDGE* | X | X | – |
| MARYLAND BRIDGE* | X | X | – |
| TELESCOPIC CROWN | X | X | X |
| CUSTOM ABUTMENT | X | X | X |
| VENEER | – | – | X |
* Except for patient with bruxism
** Possible, not recommended. Less than3 sequential pontics for the anterior.Less than 2 sequential pontics for the posterior.
| CHARACTERISTIC | HT-WHITE | ST-WHITE | TT-WHITE |
| DENSITY BEFORE SINTERING | 3.1±0.5g/cm3 | 3.1±0.5g/cm3 | >2.8g/cm3 |
| DENSITY AFTER SINTERING | 6.08±0.01 g/cm3 | 6.08±0.01 g/cm3 | 6.04±0.03 g/cm3 |
| 3-POINT FLEXURAL STRENGTH AFTER SINTERING | 1400 Mpa | 1200 Mpa | >600 Mpa |
| CHEMICAL SOLUBILITY AFTER SINTERING | < 100µg/cm2 | < 100µg/cm2 | < 100µg/cm2 |
| TRANSLUCENCY | 37% | 43% | 49% |
| RADIOACTIVITY AFTER SINTERING | <0.1 Bg/g | <0.1 Bg/g | <0.1 Bg/g |
| SINTERING TEMPERATURE | 1400-1550°C | 1400-1550°C | 1430-1470°C |
| ACCELERATED AGING SURFACE MONOCLINIC PHASE CONTENT | <15% | <15% | <5% |