AxZir Pre-shaded Zirconia Discs
axZir full-contour zirconia offers dental technicians an efficient and reliable method for producing aesthetic monolithic zirconia restorations.
Our system consists of two varieties of pre-shaded and multi-layer zirconia along with three choices for solid discs in a wide variety of sizes, shades, staining liquids and transparency levels.
Utilizing our pre-shaded discs, dental professionals can simply and consistently produce all 16 Vita A-D shades as well as bleach shades. No dipping or use of coloring liquids is required at any point in the process, helping to ensure a consistent aesthetic result.
Three different materials are available:
- HT Zr -- Normal translucent zirconia, for crown and bridges
- ST Zr -- Super translucent zirconia, for crowns and bridges especially full contour crowns and bridges
- TT Zr – Top translucent zirconia suitable for anterior full-contour restorations
Multi-layered and pre-colored discs are also available. Colored zirconia blocks are available in LL1, LL2, LL3, LL4, LL5. Or A1-D4 vita 16 classical shades
| CHARACTERISTIC | HT-COLOR | ST-COLOR |
| DENSITY BEFORE SINTERING | 3.1±0.5g/cm3 | 3.1±0.5g/cm3 |
| DENSITY AFTER SINTERING | 6.08±0.01 g/cm3 | 6.08±0.01 g/cm3 |
| 3-POINT FLEXURAL STRENGTH AFTER SINTERING | 1100 Mpa | 1100Mpa |
| CHEMICAL SOLUBILITY AFTER SINTERING | < 100µg/cm2 | < 100µg/cm2 |
| TRANSLUCENCY | 23%-35% | 34%-38% |
| RADIOACTIVITY AFTER SINTERING | <0.1 Bg/g | <0.1 Bg/g |
| SINTERING TEMPERATURE | 1480-1580°C | 1500-1580°C |
Download the HT and ST Pre-shaded Usage Instructions
AxZir ST-Color Shaded Dental Zirconia
These blanks are distinguished by their enhanced strength and long-term hydrothermal stability. An absolutely homogenous structure is achieved through a specially developed production process.
The blanks are optimised for rapid milling strategies and provide excellent edge stability and green body breaking strength during processing.
AxZir Pre-shaded biological nano zirconia discs ar made with pre-dyeing treatment of ST or HT zirconia blanks, maintaining excellent physical performance, quick milling and significant processing advantages.