AxZir HT-White Dental Zirconia

Manufacturer: AxZir
SKU: DEN-AXZIR-HT-WHT
AxZir HT-White Dental Zirconia AxZir Discs are optimized for open systems. All blanks consist of pre-sintered zirconium dioxide stabilized with yttrium oxide (3Y-TZP-A).

These blanks are distinguished by their enhanced strength and long-term hydro-thermal stability. An absolutely homogeneous structure is achieved through a specially developed production process.

The blanks are optimized for rapid milling strategies and provide excellent edge stability and green body breaking strength during processing.

Download the Usage Instructions

Download the AxZir ST, HT & TT Sintering Instructions

Download the Catalog

*
 
€41.63
  • subtitles Full description

     

    HT-WHITE- Highly translucent zirconia, for copings and frameworks

    5 Shade Liquids are Available: LL1-LL5

     

     

     

     
    INDICATION HT-WHITE ST-WHITE TT-WHITE
    COPINGS X X X
    2-4 UNIT FRAMEWORKS X X 2-3 UNITS
    5-6 UNIT FRAMEWORKS** X X -
    CANTILEVER BRIDGE* X X -
    INLAY BRIDGE* X X -
    MARYLAND BRIDGE* X X -
    TELESCOPIC CROWN X X X
    CUSTOM ABUTMENT X X X
    VENEER - - X

    * Except for patient with bruxism

    ** Possible, not recommended. Less than3 sequential pontics for the anterior.Less than 2 sequential pontics for the posterior.

     


     

    CHARACTERISTIC HT-WHITE ST-WHITE TT-WHITE
    DENSITY BEFORE SINTERING 3.1±0.5g/cm3 3.1±0.5g/cm3 >2.8g/cm3
    DENSITY AFTER SINTERING 6.08±0.01 g/cm3 6.08±0.01 g/cm3 6.04±0.03 g/cm3
    3-POINT FLEXURAL STRENGTH AFTER SINTERING 1400 Mpa 1200 Mpa >600 Mpa
    CHEMICAL SOLUBILITY AFTER SINTERING < 100µg/cm2 < 100µg/cm2 < 100µg/cm2
    TRANSLUCENCY 37% 43% 49%
    RADIOACTIVITY AFTER SINTERING <0.1 Bg/g <0.1 Bg/g <0.1 Bg/g
    SINTERING TEMPERATURE 1400-1550°C 1400-1550°C 1430-1470°C
    ACCELERATED AGING SURFACE MONOCLINIC PHASE CONTENT <15% <15% <5%

     

     
     
Customers who bought this item also bought

PRIMODENT Upper Anterior Teeth

High-end multi-layer tooth line for new generation prostheses.

Ref-line teeth are made from a new composite acrylic material. The material is composed of pre-cross-linked polymer and the matrix reinforced by inorganic nano- and micro-fillers.

Compared to conventional acrylic, the new Ref-line material offers improved resistance to the mechanical wear, good resistance to plaque adhesion, color stability, higher hardness, excellent polishing properties and good adhesion to denture base materials.

Set of 6 Teeth

Download the Mold Chart

PRIMODENT Lower Anterior Teeth

High-end multi-layer tooth line for new generation prostheses.

Ref-line teeth are made from a new composite acrylic material. The material is composed of pre-cross-linked polymer and the matrix reinforced by inorganic nano- and micro-fillers.

Compared to conventional acrylic, the new Ref-line material offers improved resistance to the mechanical wear, good resistance to plaque adhesion, color stability, higher hardness, excellent polishing properties and good adhesion to denture base materials.

Set of 6 Teeth

Download the Mold Chart

PRIMODENT Posterior Teeth

High-end multi-layer tooth line for new generation prostheses.

Ref-line teeth are made from a new composite acrylic material. The material is composed of pre-cross-linked polymer and the matrix reinforced by inorganic nano- and micro-fillers.

Compared to conventional acrylic, the new Ref-line material offers improved resistance to the mechanical wear, good resistance to plaque adhesion, color stability, higher hardness, excellent polishing properties and good adhesion to denture base materials.

Set of 8 Teeth

Download the Mold Chart